ASTM D7869-13新标准规定的氙弧灯辐照度在 0.4-0.8 W/m2@340nm 之间，在几个黑暗试验阶段向样品喷水，在实验过程中涂层会吸收和释放水份。干/湿和冷/热循环会使材料的机械应力产生变化。这些测试条件模拟亚热带气候（例如南佛罗里达）条件下涂层材料的物理和化学应力
|10||重复6-9 阶段3 次（24 小时为一个循环）|
Significance and Use
5.1 This test procedure is used to simulate the physical and environmental stresses that a coating for exterior transportation applications (for example, automotive) is exposed to in a subtropical climate, such as southern Florida. It has been found that such a subtropical climate causes particularly severe deterioration of such coatings. The long water exposures and wet/dry cycling found in southern Florida are particularly important for this deterioration, in addition to the high dosage of solar radiation (3). This practice was developed to address the deficiencies of historical tests used for transportation coatings, especially automotive coatings (4).
Note 1—This test procedure was developed through eight years of cooperative testing between automotive and aerospace OEM’s, material suppliers, and test equipment manufacturers. See References for published papers on this research.
1.1 This practice specifies the operating procedures for a controlled irradiance xenon arc light and water apparatus. The procedure uses one or more lamp(s) and optical filter(s) to produce irradiance similar to sunlight in the UV and visible range. It also simulates the water absorption and stress cycles experienced by automotive exterior coatings under natural weathering conditions. This practice has also been found applicable to coatings on other transportation vehicles, such as aircraft, trucks and rail cars.
1.2 This practice uses a xenon arc light source with specified optical filter(s). The spectral power distribution (SPD) for the lamp and special daylight filter(s) is as specified in Annex A1. The irradiance level used in this practice varies between 0.40 and 0.80 W/(m2·nm) at 340 nm. Water is sprayed on the specimens during portions of several dark steps. The application of water is such that the coatings will absorb and desorb substantial amounts of water during testing. In addition, the cycling between wet/dry and warm/cool will induce mechanical stresses into the materials. These test conditions are designed to simulate the physical and chemical stresses from environments in a subtropical climate, such as southern Florida.
1.3 The values stated in SI units are to be regarded as standard. No other units of measurement are included in this standard.
1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.
D4517 Test Method for Low-Level Total Silica in High-Purity Water by Flameless Atomic Absorption Spectroscopy
G113 Terminology Relating to Natural and Artificial Weathering Tests of Nonmetallic Materials
G147 Practice for Conditioning and Handling of Nonmetallic Materials for Natural and Artificial Weathering Tests
G151 Practice for Exposing Nonmetallic Materials in Accelerated Test Devices that Use Laboratory Light Sources
G155 Practice for Operating Xenon Arc Light Apparatus for Exposure of Non-Metallic Materials
以上标准信息来自互联网搜索整理，如需了解完整的ASTM D7869的信息或ASTM D7869标准解读，欢迎致电【400-6808-138】详询。
Q-SUN B02-S日晒色牢度仪是专为纺织品设计的色牢度检测仪，同时也是最可靠、最易用、最被广泛认可的日晒气候色牢度仪。（目前已经更新为Q-SUN Xe-2）Q-SUN B02-S(Xe-2) 马上询价
Q-SUN Xe-3-HCE是一款具有全光谱光照模拟、湿度控制以及制冷功能的氙灯老化试验机,其命名规则为湿度控制（H）、制冷功能（C）。Q-SUN Xe-3-HCE 马上询价
Q-SUN Xe-3-HDSE氙灯耐气候试验箱具有湿度控制、以及双喷淋功能,其命名规则为湿度(H)、双喷淋(D)、喷淋(S)。Q-SUN Xe-3-HDSE 马上询价
Q-SUN Xe-3-HSCE氙灯耐候试验箱同时具有湿度控制、喷淋以及制冷功能，其命名规则为湿度(H)、喷淋(S)、制冷(C)。Q-SUN Xe-3-HSCE 马上询价